Author: Gordon (NZ)
Date: 2001-07-16 12:14
If acid perspiration was the problem I would expect pitting, not wear.
We know from silver plated cutlery which gets significant wear, that this thick plating can last many years.
It seems very clear that you have a "decorative" plating rather than a servicable plating, which should be many, many times thicker. Get it replaced under guarantee, the sooner the beter. It is probably a bad batch that the manufacturer already knows about.
|
|